Drier stabilizer for oxidatively drying paint systems

  • Physical Characteristics

    Metal contentCo: 20.80 – 21.30
    % ASTM D 2373
    Non-volatile content75 – 85 % ASTM D
    1644 B
    ViscosityMax 100 s MCI 76-
    72
    Specific gravity1.160 – 1.220
    (25°C) ASTM D
    1963
    DensityNA

  • Features

    • Countervails adsorption of active drier during prolonged
    storage
    • Does not need initial excessive addition of driers
    • which often could lead to defects
    • Does not affect initial drying of the paint system
    • Has no adverse effect on the film properties of the pain

  • Applications

    • Oxidative solvent-based systems
    • Some water-reducible systems
    • Aqueous systems when the system contains an appropriate co-solvent

  • Dosage

    21% Cobalt Hydroxy Ten-Cem® is added to the milling base with pigment and binder. Subsequent addition is also
    possible. The addition of 21% Cobalt Hydroxy Ten-Cem® ranges between 0.3 and 0.7 %, relative to the solid binder. The
    optimum amount must always be determined individually beforehand in trials.

  • Storage

    Protect from the effects of weathering and store at temperatures below 50 °C. Once opened, containers should be resealed
    immediately after each removal of the product. During storage an increase in paste viscosity could be observed. The product
    should be stirred before using.

  • Safety

    Protect from the effects of weathering and store at temperatures below 50 °C. Once opened, containers
    should be resealed immediately after each use.

Registration :
  • Europe : EINECS
  • Switzerland : EINECS
  • Norway : +
  • USA : TSCA
  • Canada : DSL
  • Australia : AICS
  • China : IECSC
  • Japan : ENCS
  • Korea : ECL
  • Taiwan : NECI
Multimedia